| Polyether block amide Pebax® MH 2030 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide. Pebax® MH 2030 resin is an inherently dissipative polymer and can be dry blended or compounded with an isolative polymer to lower the surface resistivity of the final part.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA12弹性体 |
| Material Status | Commercial: Active |
| Features | Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 4.5 | % | ISO 62 |
| 23℃，24hr | 120 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 40 | ISO 868 | |
| Bending modulus | 80.0 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 200 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+7 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+7 | ohms·cm | IEC 60093 |
| Charge Decay Time | < 1.0 | sec | MIL B-81705 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.508 | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Processing (melt) temperature | 230 to 260 | °C | |
| Mold temperature | 25 to 60 | °C | |
| Drying temperature | 70 to 90 | °C | |
| Drying time | 5.0 to 7.0 | hr | |
| Melt temperature | 230 to 280 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |