| Versaflex™ CE 3115 is targeted for consumer electronics applications where excellent abrasion resistance, chemical resistance and silky feel are required. Versaflex™ CE 3115 can also overmold to a variety of substrates including PC, ABS, PC/ABS, and Copolyester.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good surface appearance,Low coefficient of friction,Good wear resistance,Solvent resistance,Good coloring,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds | 65 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 15.2 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 3.07 | MPa | ASTM D412 |
| 300% Strain, 73°F | 5.10 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 640 | % | ASTM D412 |
| tear strength | |||
| 23℃ | 52.5 | kN/m | ASTM D624 |
| Compression deformation | |||
| 23℃，22 hr | 24 | % | ASTM D395 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.5 to 13.0 mm, all | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Mass Loss（500 Cycle Abrasion Resistance，23℃） | 2.0 | mg | ASTM D3389 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 1.0 to 12 | g/10min | ASTM D1238 |
| 200℃，5.0kg | 15 to 25 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：193℃ | 0.90 to 1.5 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 16.0 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 52 to 60 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.030 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 171 to 182 | °C | |
| Barrel middle temperature | 182 to 210 | °C | |
| Barrel front temperature | 188 to 216 | °C | |
| Nozzle temperature | 193 to 221 | °C | |
| Processing (melt) temperature | 193 to 218 | °C | |
| Mold temperature | 13 to 29 | °C | |
| Back pressure | 0.00 to 0.345 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 4. 25% deflection |
| 5. Abrasion wheel: H-18 Mass Lost |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |