| About |
|---|
| The Versaflex™ OM 1360-9 is designed for overmolding onto polycarbonate (PC), ABS, and PC/ABS susbstrates. Excellent Bond to PC, ABS, PC/ABS Rubbery Feel Soft Touch&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Renewable resources |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 10 seconds, 23 ℃ | 60 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D412 | ||
| Fracture, 23 ℃ | 6.89 | MPa | ASTM D412 |
| 100% strain, 23 ℃ | 1.79 | MPa | ASTM D412 |
| 300% Strain, 73°F | 3.65 | MPa | ASTM D412 |
| Tensile strain | |||
| Fracture, 23 ℃ | 650 | % | ASTM D412 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.90 to 2.1 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，11200 sec^-1 | 16.0 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 43 to 46 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.030 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 160 to 193 | °C | |
| Barrel middle temperature | 177 to 193 | °C | |
| Barrel front temperature | 182 to 204 | °C | |
| Nozzle temperature | 193 to 216 | °C | |
| Processing (melt) temperature | 182 to 216 | °C | |
| Mold temperature | 21 to 32 | °C | |
| Back pressure | 0.00 to 0.862 | MPa | |
| Screw speed | 75 to 125 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. 2 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |