| NORYL NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptional balance of strength and dimensional stability. This grade can be processed via extrusion or injection molding. NORYL NH8006 is available in custom colors and may be an excellent material candidate for use in electrical and electronics markets.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability,Halogen free,Flame Characteristics |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 1.33 | g/cm³ | ASTM D792 |
| — | 1.34 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 2.1 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，10 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 to 0.25 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.23 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.070 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 9500 | MPa | ASTM D638 |
| — | 9000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 125 | MPa | ASTM D638 |
| yield | 125 | MPa | ISO 527-2/5 |
| fracture | 125 | MPa | ASTM D638 |
| fracture | 125 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 2.0 | % | ASTM D638 |
| yield | 1.8 | % | ISO 527-2/5 |
| fracture | 2.0 | % | ASTM D638 |
| fracture | 1.8 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 8600 | MPa | ASTM D790 |
| — | 8000 | MPa | ISO 178 |
| bending strength | |||
| — | 160 | MPa | ISO 178 |
| Yield, 50 mm span | 185 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 9.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 75 | J/m | ASTM D256 |
| 23℃ | 85 | J/m | ASTM D256 |
| -30℃ | 8.0 | kJ/m² | ISO 180-1A |
| 23℃ | 8.0 | kJ/m² | ISO 180-1A |
| Notched impact strength of cantilever beam | |||
| 23℃ | 500 | J/m | ASTM D4812 |
| 23℃ | 26 | kJ/m² | ISO 180/1U |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 14.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 149 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 149 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 156 | ℃ | ASTM D1525 10 |
| B120 | 160 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 3.7E-5 | 1/℃ | ASTM E831 |
| TD：-40~40℃ | 5.5E-5 | 1/℃ | ASTM E831 |
| TD：-40℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| Relative temperature index | 110 | ℃ | UL 746 |
| Electrical performance | 110 | ℃ | UL 746 |
| Impact mechanical performance | 105 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | |||
| — | > 4.0E+17 | ohms | ASTM D257 |
| — | 4.0E+17 to 5.0E+17 | ohms | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 16 | kV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 1 MHz | 3.11 | ASTM D150 | |
| 1 MHz | 3.10 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 4.0E-3 | ASTM D150 | |
| High Arc Burning Index (HAI) | PLC 4 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 0 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-1 | ||
| 2.00 mm | V-0 | ||
| 3.00 mm | |||
| Glowing wire flammability index | |||
| 3.2 mm | 960 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 80 to 100 | °C | |
| Barrel rear temperature | 260 to 280 | °C | |
| Barrel middle temperature | 280 to 300 | °C | |
| Barrel front temperature | 300 to 320 | °C | |
| Nozzle temperature | 280 to 300 | °C | |
| Processing (melt) temperature | 300 to 320 | °C | |
| Mold temperature | 100 to 130 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. at Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 mm |
| 9. Rate A (50°C/h), Loading 2 (50 N) |
| 10. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |