| About |
|---|
| Product Description | |
|---|---|
| Supplier | TEIJIN |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ISO 1133 |
| Melt Volume Rate | |||
| 300℃，1.2 kg | 8 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.5-0.7 | % | Internal Method |
| TD | 0.5-0.7 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1 mm/min | 2400 | MPa | ISO 527-1 |
| tensile strength | |||
| Yield, 50 mm/min | 61 | % | ISO 527-1 |
| Tensile strain | |||
| Yield, 50 mm/min | 6 | % | ISO 527-2 |
| Tensile strain | |||
| Fracture, 50 mm/min | >50 | ISO 527-2 | |
| bending strength | |||
| 2 mm/min | 93 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/mim | 2350 | MPa | ISO 178 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Capacitance | |||
| 100Hz | 3.1 | IEC 60250 | |
| 1MHz | 3 | IEC 60250 | |
| Dielectric loss angle | |||
| 100Hz | 10 | ×10 -4 | IEC 60250 |
| 1MHz | 90 | ×10 -4 | IEC 60250 |
| Volume resistivity | >1E+15 | ohms·cm | IEC 60093 |
| Surface resistivity | ＞5.0E+15 | ohms | IEC 60093 |
| Voltage resistance | |||
| short-term | 30 | MV/m | |
| Electrical trace resistance | 250 | IEC 60112 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | |||
| Parallel flow | 0.7 | ×10 -4 /k | ISO 11359-2 |
| Transverse flow | 0.7 | ×10 -4 /k | ISO 11359-2 |
| Hot deformation temperature | |||
| 0.45 MPa | 142 | ℃ | ISO 75 |
| 1.8 MPa | 129 | ℃ | ISO 75 |
| Vicat Softening Temp | |||
| B50 | 149 | ISO 306 | |
| Relative temperature index, 1.47mmt | |||
| Electrical performance | 125 | ℃ | UL 746B |
| Mechanical impact characteristics | 115 | ℃ | UL 746B |
| Non mechanical impact performance | 125 | ℃ | UL 746B |
| Flame retardant level | |||
| 0.40 mm | V-2 | UL 94 | |
| 1.50 mm | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.585 | ASTM D542 | |
| Transmittance | |||
| 3 mm | 88 | % | ASTM D1003 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| NB | kJ/m² | ISO 179 | |
| 76 | kJ/m² | ISO 179 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |