| About |
|---|
| Polyamide 66 alloy, 40% glass fiber, improved flowability, heat stabilized, for injection moulding, black |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA66 Alloy |
| Material Status | Commercial: Active |
| Features | Good liquidity,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.46 | g/cm³ | |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 0.55 | % | |
| TD：23℃，72 hrs | 0.15 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 4.5 | % | |
| Equilibrium, 23 ℃, 50% RH | 1.5 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 13800 | MPa | |
| Tensile stress (fracture) | 230 | MPa | |
| Tensile strain | |||
| fracture | 3.0 | % | |
| Bending modulus | 12500 | MPa | |
| Bending stress | 360 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 13 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 130 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 235 | ℃ | |
| Melting temperature | 262 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | > 1.0E+12 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 280 to 305 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |