| About |
|---|
| PPE+PS blend. Unfilled. Suitable for profile extrusion. Low water absorption. Hydrolytic stability. Dimensional stability. Typical applications include tubes for reverse osmosis systems.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Hydrolysis stability,Low or no water absorption,HB |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 280℃，5.0kg | 8.5 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 280℃，5 kg | 8.70 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| 24hr | 0.060 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30℃ | 10 | kJ/m² | ISO 179/2C |
| 23℃ | 13 | kJ/m² | ISO 179/2C |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -30℃ | 110 | J/m | ASTM D256 |
| 23℃ | 190 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 8.7 | kJ/m² | ISO 180-1A |
| 23℃ | 13 | kJ/m² | ISO 180-1A |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 39.0 | J | ASTM D3763 |
| Drop hammer impact | ASTM D3029 | ||
| -40℃ | 5.42 | J | ASTM D3029 |
| -30℃ | 25.8 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.2 mm | 118 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 126 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 3.2 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 6.4 mm | 137 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 137 | ℃ | ISO 306 |
| B120 | 141 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-40~95℃ | 5.9E-5 | 1/℃ | ASTM E831 |
| Relative temperature index | |||
| Electrical performance | 105 | ℃ | UL 746 |
| Strength mechanical performance | 105 | ℃ | UL 746 |
| Impact mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 3.2 mm in oil | 20 | kV/mm | ASTM D149 |
| Dielectric constant | ASTM D150 | ||
| 50 Hz | 2.65 | ASTM D150 | |
| 60 Hz | 2.65 | ASTM D150 | |
| Dissipation factor | ASTM D150 | ||
| 50 Hz | 4.0E-4 | ASTM D150 | |
| 60 Hz | 4.0E-4 | ASTM D150 | |
| Arc resistance | PLC 7 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 3 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ASTM D638 |
| Tensile modulus | 2550 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 50.0 | MPa | ASTM D638 |
| fracture | 50.0 | MPa | ISO 527-2 |
| yield | 56.0 | MPa | ASTM D638 |
| yield | 55.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 28 | % | ASTM D638 |
| fracture | 27 | % | ISO 527-2 |
| yield | 3.3 | % | ASTM D638 |
| yield | 3.1 | % | ISO 527-2 |
| Bending modulus | ASTM D790 | ||
| 50 mm span | 2550 | MPa | ASTM D790 |
| 100 mm span | 2450 | MPa | ASTM D790 |
| Bending modulus | 2500 | MPa | ISO 178 |
| bending strength | 95.0 | MPa | ISO 178 |
| bending strength | ASTM D790 | ||
| Yield, 50 mm span | 89.0 | MPa | ASTM D790 |
| Yield, 100 mm span | 88.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 119 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 104 to 116 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 204 | °C | |
| Barrel 2 zone temperature | 204 | °C | |
| Barrel 3 zone temperature | 227 | °C | |
| Barrel 4 zone temperature | 227 | °C | |
| Connector temperature | 249 | °C | |
| Melt temperature | 227 to 254 | °C | |
| Nozzle temperature | 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.10 in/min |
| 5. 0.051 in/min |
| 6. 80*10*4 mm |
| 7. Tungsten Electrode |
| 8. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |