| KOPA® KN133G15HS是一种聚酰胺6（尼龙6）产品,含有的填充物为15% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 良好的尺寸稳定性 耐热&& |
| Product Description | |
|---|---|
| Supplier | Kolon |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,High Heat Resistance,HB |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| MD | 0.70 to 0.90 | % | ASTM D955 |
| TD | 0.67 | % | ISO 294-4 |
| MD | 0.66 | % | ISO 294-4 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 60% RH | 0.40 | % | ASTM D570 |
| 23℃，24hr | 3.8 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 190 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 180 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 205 | ℃ | ASTM D648 |
| Melting peak temperature | 220 | ℃ | ASTM D3418 |
| Melting temperature | 225 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 21 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 3.60 | ASTM D150 | |
| Arc resistance | 130 | sec | ASTM D495 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 130 | MPa | ISO 527-2 |
| 23℃ | 123 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ISO 527-2 |
| Fracture, 23 ℃ | 8.0 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 5200 | MPa | ISO 178 |
| 23℃ | 5440 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 196 | MPa | ASTM D790 |
| 23℃ | 170 | MPa | ISO 178 |
| Rockwell hardness | |||
| R-level | 120 | ASTM D785 | |
| R-level | 120 | ISO 2039-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 to 100 | °C | |
| Drying time – hot air dryer | 4.0 to 5.0 | hr | |
| Recommended maximum moisture content | < 0.050 | % | |
| Barrel rear temperature | 230 | °C | |
| Barrel middle temperature | 240 | °C | |
| Barrel front temperature | 245 | °C | |
| Nozzle temperature | 250 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |