| About |
|---|
| SD POLYCA™ IM6000 series are PC/ABS alloy grades. These grades have excellent properties of both polycarbonate and ABS resins such as high impact strength, heat stability and good processing latitude in injection molding. We prepare variety of products to cover your applications. |
| Product Description | |
|---|---|
| Supplier | Sumitomo |
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Heat Stabilized |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，5 kg | 6.00 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | |
| TD | 0.50 to 0.70 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 50 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 640 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 128 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 100 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 7.0E-5 | 1/℃ | |
| TD | 7.0E-5 | 1/℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 118 | ASTM D785 | |
| Tensile modulus | 2300 | MPa | ISO 527-2 |
| tensile strength | |||
| — | 49.0 | MPa | ASTM D638 |
| — | 52.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 110 | % | ASTM D638 |
| fracture | 100 | % | ISO 527-2 |
| Bending modulus | |||
| — | 1960 | MPa | ASTM D790 |
| — | 2300 | MPa | ISO 178 |
| bending strength | |||
| — | 73.0 | MPa | ASTM D790 |
| — | 70.0 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |