| About |
|---|
| Ketron® PEEK-CA30 is a Polyetheretherketone (PEEK) product filled with 30% carbon fiber. It can be processed by extrusion and is available in Latin America or North America. Characteristics include: Flame Rated Conductive&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good wear resistance,Thermal conductivity,V-0 |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.30 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.14 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Continuous use temperature | |||
| — | 250 | ℃ | |
| — | 310 | ℃ | |
| Melting temperature | |||
| DSC | 340 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 23 to 100 ℃ | 2.5E-5 | cm/cm/℃ | |
| 23 to 150 ℃ | 2.5E-5 | cm/cm/℃ | |
| > 150℃ | 5.5E-5 | cm/cm/℃ | |
| Thermal conductivity coefficient | |||
| 23℃ | 0.92 | W/m/K |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | < 1.0E+5 | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 40 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-grade, 10.00 mm | 102 | ISO 2039-2 | |
| Ball hardness | |||
| 10.0 mm | 325 | MPa | ISO 2039-1 |
| Tensile modulus | 7700 | MPa | ISO 527-2/1B/1 |
| tensile strength | |||
| fracture | 130 | MPa | ISO 527-2/1B/5 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2/1B/5 |
| compressive strength | ISO 604/1 | ||
| 1% strain | 49.0 | MPa | ISO 604/1 |
| 2% strain | 97.0 | MPa | ISO 604/1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 3. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |