| About |
|---|
| Ultrason® pellets are supplied in bags and/or octabins. The bulk density ranges between 700 and 800 g/l. Provided the packaging remains undamaged, Ultrason® can be stored indefinitely. Ultrason® pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 4h at 130°C to 150°C in a vacuum or dry air drier prior to processing.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PES |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.50 | g/cm³ | ISO 1183 |
| Apparent density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume Rate | |||
| 360℃，10 kg | 29.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.61 | % | ISO 294-4 |
| MD | 0.36 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.6 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.60 | % | ISO 62 |
| Viscosity number | 56.0 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 47 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23℃ | 6.5 | kJ/m² | ISO 180-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 220 | ℃ | ISO 75-2/A |
| Glass transition temperature | 225 | ℃ | ISO 11357-2 |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 23 to 80 ℃ | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 180℃ | 2.3E-5 | cm/cm/℃ | DIN 53752 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Polymer Abbreviation | PESU-GF20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H 961/30 | 205 | MPa | ISO 2039-1 |
| Tensile modulus | 7300 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 140 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 80 | °C | |
| Barrel rear temperature | 350 | °C | |
| Barrel middle temperature | 360 | °C | |
| Barrel front temperature | 370 | °C | |
| Nozzle temperature | 370 | °C | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 150 to 190 | °C | |
| Screw Speed | < 300 | mm/sec | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. in 0,01 g/ml Phenol/1,2, ortho-Dichlorbenzol, 1:1 |
| 3. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |