| APTIV® 1300 film is the black version of unfilled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications offering an alternative option to the APTIV 1000 natural product. APTIV 1300 film has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products and low moisture absorption in a film format. Inherently halogen free and providing ease of processing makes APTIV films a technology enabler for OEMs, our customers and end users.&& |
| Product Description | |
|---|---|
| Supplier | Victrex |
| Material Status | Commercial: Active |
| Features | Good Printability,Welding,Hypocrystalline,Low smoke,Electroplating,Good heat sealing,Excellent Processability,Solvent resistance,Hydrolysis stability,High Heat Resistance,Low moisture absorption,Halogen free,Low toxicity,Durability,Good flexibility,Renewable resources,High purity,Gamma radiation,Good Rigidity,Insulation,Flame Characteristics,Block resin,Good wear resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding shrinkage | |||
| MD：200℃，50.0 µm | < 2.0 | % | |
| TD：200℃，50.0 µm | < 2.0 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Film thickness | 50 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD，23℃，50 µm | 2500 | MPa | ISO 527-3 |
| TD，23℃，50 µm | 2500 | MPa | ISO 527-3 |
| MD，23℃，100 µm | 2400 | MPa | ISO 527-3 |
| TD，23℃，100 µm | 2300 | MPa | ISO 527-3 |
| Tensile Strength | ISO 527-3 | ||
| MD, fracture BRK, 23 ℃, 50 µ m | 120 | MPa | ISO 527-3 |
| TD, fracture BRK, 23 ℃, 50 µ m | 110 | MPa | ISO 527-3 |
| MD, fracture BRK, 23 ℃, 100 µ m | 120 | MPa | ISO 527-3 |
| TD, fracture BRK, 23 ℃, 100 µ m | 110 | MPa | ISO 527-3 |
| Tensile Strain | ISO 527-3 | ||
| MD, fracture BRK, 23 ℃, 50 µ m | > 150 | % | ISO 527-3 |
| TD, fracture BRK, 23 ℃, 50 µ m | > 150 | % | ISO 527-3 |
| MD, fracture BRK, 23 ℃, 100 µ m | > 150 | % | ISO 527-3 |
| TD, fracture BRK, 23 ℃, 100 µ m | > 150 | % | ISO 527-3 |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume Resistance | |||
| 23 ℃，0.05 mm | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | |||
| 23 ℃，0.05 mm | 190 | kV/mm | ASTM D149 |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Puncture Resistance | |||
| 23℃，50.0 µm | 5.00 | kJ/m² | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. TM-VX-84 |
| 3. 100 V |
| 4. 6.25 mm electrode |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |