AFFINITY™ PT 1450G1

About
Monolayer and coextrusion coating for packaging applications Recommended for use with Oriented Polypropylene (OPP as a tie layer or sealant) Coextruded with acid copolymer as a cost effective foil or PET sealant Complies with U.S. FDA Consult the regulations for complete details. (See NOTES) AFFINITY™ PT 1450G1 Polyolefin Plastomer is produced via INSITE™ Technology. It is an ethylene alpha-olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, ultimate seal strength, adhesion to (OPP) and good taste and odor performance. Note: It is the responsibility of the manufacturer of the food contact article to ensure the article is suitable for its intended use. Manufacturers should be aware that foods with a high oil content may compromise the integrity of the packaging.&&

About

Monolayer and coextrusion coating for packaging applications Recommended for use with Oriented Polypropylene (OPP as a tie layer or sealant) Coextruded with acid copolymer as a cost effective foil or PET sealant Complies with U.S. FDA Consult the regulations for complete details. (See NOTES) AFFINITY™ PT 1450G1 Polyolefin Plastomer is produced via INSITE™ Technology. It is an ethylene alpha-olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, ultimate seal strength, adhesion to (OPP) and good taste and odor performance. Note: It is the responsibility of the manufacturer of the food contact article to ensure the article is suitable for its intended use. Manufacturers should be aware that foods with a high oil content may compromise the integrity of the packaging.&&

Product Description
Supplier	DOW
Generic	POP
Material Status	Commercial: Active
Availabilitys	North America,Latin America,Asia Pacific
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.902	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	7.5	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
Initial sealing temperature
25 µm	82.8	℃	Internal Method
Can be bonded to OPP			Internal Method
316℃	0.13	kN/m	Internal Method
288℃	0.18	kN/m	Internal Method

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	77.2	℃	ASTM D1525
Melting temperature
DSC	97.8	℃	Internal Method

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	288 to 316	°C
Shrinkage (316°C, 25.4 μm)	134.6	mm
Minimum coating thickness	< 7.6	µm
Minimum coating weight	< 7.3	g/m²

Notes
1. Typical properties: these are not to be construed as specifications.
2. 1.0 mil (25µm) coating. Temperature at which 1 lb/in. (4.4 N/25.4 mm) heat seal strength is achieved. Heat Seal Strengths, Topware HT Tester, 0.5 S dwell, 40 psi bar pressure, pull speed 150 mm/sec.
3. 1.0 mil (25µm) coating onto 50 lb Kraft paper.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.