| PARYLS® mPPSU M1150 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® mPPSU M1150 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 160 °C in a vacuum or dry air drier prior to processing. Features PARYLS® mPPSU is a modified polyphenylsufone. It is a high-heat, high performance resin formulation exhibiting very good hydrolytic stability, excellent resistance to scids and bases and good resistance to stress cracking under a broad range of chemical environments. In addition, PARYLS® mPPSU resin exhibits robust toughness and improved notch resistance compared to both PARYLS® PSU and PARYLS® PES, although slightly lower than that of neat PARYLS® PPSU. In general, the performance profile of PARYLS® mPPSU resin falls between PSU and PPSU, and also offers very good electrical properties over a broad temperature range as well as inherent flam retardancy, offers better cost-efficiency advantage also. Natural: mPPSU M1150NT, Black: mPPSU M1150BK, White: mPPSU&& |
| Product Description | |
|---|---|
| Supplier | Youju |
| Generic | PPSU |
| Material Status | Commercial: Negative |
| Features | Good Electrical Properties,Hydrolysis stability,Flame Characteristics,Acidproof,High Heat Resistance,High ESCR |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 380℃，2.16kg | 15 to 20 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 , ISO 2577 | ||
| TD | 0.80 | % | ISO 294-4，ISO 2577 |
| MD | 0.70 | % | ISO 294-4，ISO 2577 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.30 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2690 | MPa | ISO 527-2 |
| tensile strength | 75.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| yield | 7.0 | % | ISO 527-2 |
| Bending modulus | 2400 | MPa | ISO 178 |
| bending strength | 105 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 10 | kJ/m² | ISO 180/A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 195 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | 44 | kV/mm | ASTM D149 |
| Dielectric constant | IEC 60250 | ||
| 100 Hz | 3.80 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation factor | IEC 60250 | ||
| 100 Hz | 1.5E-3 | IEC 60250 | |
| 1 MHz | 8.6E-3 | IEC 60250 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 160 | °C | |
| Drying time | 6.0 | hr | |
| Processing (melt) temperature | 350 to 390 | °C | |
| Mold temperature | 140 to 160 | °C | |
| Drying temperature | 160 | °C | |
| Drying time | 6.0 | hr | |
| Melt temperature | 350 to 390 | °C | |
| Nozzle temperature | 140 to 160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 100V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |