| Quadrant EPP Fluorosint® 500 is a Polytetrafluoroethylene (PTFE) product filled with mica. It can be processed by compression molding and is available in Latin America or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Quadrant |
| Generic | PTFE |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Dimensional Stability,Good Electrical Properties,Low coefficient of friction,Flame Characteristics,High Heat Resistance,Non-abrasive ,Good wear resistance,Solvent resistance,V-0 |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 2.32 | g/cm³ | ISO 1183 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.5 to 2.5 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | < 0.10 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.5 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 8.0 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 130 | ℃ | ISO 75-2/A |
| Melting temperature | |||
| DSC | 327 | ℃ | ISO 11357 |
| Linear coefficient of thermal expansion | |||
| MD | |||
| 23 to 100 ℃ | 5.0E-5 | cm/cm/℃ | |
| 23 to 150 ℃ | 5.5E-5 | cm/cm/℃ | |
| > 150℃ | 8.5E-5 | cm/cm/℃ | |
| Thermal conductivity coefficient | |||
| 23℃ | 0.77 | W/m/K | |
| Operating temperature | |||
| minimum | -20 | ℃ | |
| Maximum operating temperature | |||
| continuously： for min. 20，000 h | 260 | ℃ | |
| for short periods | 280 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+13 | ohms | ESD STM11.11 |
| Volume resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm in oil | 11 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 1 MHz | 2.85 | IEC 60250 | |
| Dissipation factor | |||
| 1 MHz | 8.0E-3 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | > 95 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-grade, 10.00 mm | 55 | ISO 2039-2 | |
| Ball hardness | |||
| 10.0 mm | 60.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1750 | MPa | ISO 527-2/1B/1 |
| tensile strength | ISO 527-2/1B/5 | ||
| yield | 7.00 | MPa | ISO 527-2/1B/5 |
| — | 7.00 | MPa | ISO 527-2/1B/5 |
| Tensile strain | ISO 527-2/1B/5 | ||
| yield | 5.0 | % | ISO 527-2/1B/5 |
| fracture | 15 | % | ISO 527-2/1B/5 |
| compressive strength | ISO 604/1 | ||
| 1% strain | 12.0 | MPa | ISO 604/1 |
| 2% strain | 19.0 | MPa | ISO 604/1 |
| 5% strain | 25.0 | MPa | ISO 604/1 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2000 psi |
| 3. Method A (Short-Time) |
| 4. 1-10, 1=Easier to Machine |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |