| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ISO 1183 |
| Apparent density | 0.77 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 23.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 2.0 | % | |
| MD | 1.8 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.60 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 12 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Impact strength of cantilever beam notch | |||
| 23℃ | 无断裂 | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 115 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| B50 | 125 | ℃ | ISO 306 |
| Melting temperature | 210 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 1.9E-4 | 1/℃ | |
| TD | 1.9E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric strength | 22 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 3.80 | ||
| 1 MHz | 3.40 | ||
| Dissipation factor | |||
| 100 Hz | 0.011 | ||
| 1 MHz | 0.034 | ||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 55 | ISO 868 | |
| Tensile modulus | 280 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 36.0 | MPa | |
| 5% strain | 11.9 | MPa | |
| 10% strain | 16.9 | MPa | |
| 50% strain | 18.6 | MPa | |
| 100% strain | 18.0 | MPa | |
| Nominal tensile fracture strain | 500 | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |