| About |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PPA+PA66 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | |
| TD | 0.30 to 0.50 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 11 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 70 | kJ/m² | |
| 23℃ | 80 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | > 250 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 220 | ℃ | ISO 75-2/C |
| Melting temperature | 255 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 230 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| 23℃ | > 20000 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 220 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.9 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | < 0.10 | % | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |