| About |
|---|
| Skyrol® SP81 is a one side chemically treated polyester film for improved solvent based ink adhesion. SP81 has been widely accepted for many flexible packaging applications, especially for those requiring high quality printing.&& |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good flexibility,Good Printability |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D1505 |
| Shrinkage rate | |||
| MD：150℃，0.012 mm，30 min | 1.7 | % | Internal Method |
| MD：150℃，0.023 mm，30 min | 1.6 | % | Internal Method |
| MD：150℃，0.0295 mm，30 min | 1.5 | % | ASTM D955 |
| TD：150℃，0.012 mm，30 min | 1.1 | % | Internal Method |
| TD：150℃，0.023 mm，30 min | 0.70 | % | Internal Method |
| TD：150℃，0.0295 mm，30 min | 0.90 | % | ASTM D955 |
| Surface tension – Treaded | ASTM D2578 | ||
| 12.0 µm | 50 | mN/m | ASTM D2578 |
| 23.0 µm | 50 | mN/m | ASTM D2578 |
| 29.5 µm | 50 | mN/m | ASTM D2578 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.30 | ASTM D1894 | |
| With oneself – dynamic | 0.30 | ASTM D1894 | |
| With oneself – dynamic | 0.30 | ASTM D1894 | |
| With oneself – static | 0.30 | ASTM D1894 | |
| With oneself – static | 0.40 | ASTM D1894 | |
| With oneself – static | 0.40 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D882 | ||
| MD, yield, 12 µ m | 283 | MPa | ASTM D882 |
| MD, yield, 23 µ m | 262 | MPa | ASTM D882 |
| MD, yield, 30 µ m | 255 | MPa | ASTM D882 |
| TD, yield, 12 µ m | 290 | MPa | ASTM D882 |
| TD, yield, 23 µ m | 255 | MPa | ASTM D882 |
| TD, yield, 30 µ m | 234 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 130 | % | ASTM D882 |
| MD, fracture, 23 µ m | 130 | % | ASTM D882 |
| MD, fracture, 30 µ m | 130 | % | ASTM D882 |
| TD, fracture, 12 µ m | 99 | % | ASTM D882 |
| TD, fracture, 23 µ m | 120 | % | ASTM D882 |
| TD, fracture, 30 µ m | 130 | % | ASTM D882 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | ASTM D523 | ||
| 12 µm | 166 | ASTM D523 | |
| 23 µm | 161 | ASTM D523 | |
| 29.5 µm | 162 | ASTM D523 | |
| Transmittance | ASTM D1003 | ||
| 12.0 µm | 91.0 | % | ASTM D1003 |
| 23.0 µm | 90.0 | % | ASTM D1003 |
| 29.5 µm | 90.0 | % | ASTM D1003 |
| Haze | ASTM D1003 | ||
| 12 µm | 3.2 | % | ASTM D1003 |
| 23 µm | 3.5 | % | ASTM D1003 |
| 29.5 µm | 4.1 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 29.5 µm |
| 3. 23 µm |
| 4. 12 µm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |