SABIC® HDPE ICP5703

About
SABIC® HDPE ICP5703 is part of SABIC’s high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP5703 is typically used for blow moulding UN certified Open Head drums, from 25 up to 220 liter. This food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® HDPE ICP5703 is part of SABIC’s high density polyethylene Industrial Container Product portfolio. SABIC® HDPE ICP5703 is typically used for blow moulding UN certified Open Head drums, from 25 up to 220 liter. This food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,Good tear strength,High density
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.956	g/cm³	ISO 1183
Melt Flow Rate
190℃，21.6kg	3.1	g/10min	ISO 1133
ESCR(Environmental Stress Cracking Resistance)
10% non-ionic detergent, molded, F50	110	hr	ASTM D1693B

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-30 ℃, molded	50	kJ/m²	ISO 180-A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	84.0	℃	ISO 75-2/B
Vicat Softening Temp	128	℃	ISO 306/A
Melting temperature
DSC	133	℃	ISO 11357-3
Enthalpy Change	212	J/g	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	63		ISO 868
Tensile modulus
2 mm, molded into shape	1150	MPa	ISO 527-2/1BA/50
tensile strength			ISO 527-2/1BA/50
Yield, 2 mm, molded	27.0	MPa	ISO 527-2/1BA/50
Fracture, 2 mm, molded	40.0	MPa	ISO 527-2/1BA/50
Tensile strain
Fracture, 2 mm, molded	> 1000	%	ISO 527-2/1BA/50
Bending modulus
2 mm, molded into shape	1350	MPa	ISO 178
bending strength
2 mm, molded into shape	28.0	MPa	ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.