| LUPOY PC 1302HP-10 resin is designed for extrusion products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.&& |
| Product Description | |
|---|---|
| Supplier | LG Chemical |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Clarity,High purity,High impact resistance,High Heat Resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 23℃，24hr | 0.15 | % | ASTM D570 |
| 23℃，50% RH | 0.32 | % | ASTM D570 |
| Melt Flow Rate | |||
| 300℃，1.20kg | 10 | g/10min | ASTM D1238 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Refractive index | 1.59 | ASTM D542 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze μ M | 1.1 | % | ASTM D1003 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 144 | ℃ | ASTM D648 |
| 1.8 MPa, annealed | 141 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 128 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| 149 | ℃ | ASTM D1525 | |
| Linear coefficient of thermal expansion | |||
| MD | 6.8E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 2.0E+17 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 17 | KV/mm | ASTM D149 | |
| Compared to the leakage tracing index | 250 | V | ASTM D3638 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.50 mm | V-2 | UL 94 | |
| 1.60 mm | V-2 | UL 94 | |
| 2.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 900 | J/m | ASTM D256 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 73 | M 级 | ASTM D785 |
| Rockwell hardness | 118 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 60.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 150 | % | ASTM D638 |
| Tensile modulus | |||
| 23℃ | 2410 | MPa | ASTM D638 |
| bending strength | |||
| 23℃ | 96.0 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 2410 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |