| About |
|---|
| Alkamax ML1810PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PN is formulated with a process aid and process stabilisation package. It does not contain slip or antiblocking additives. Film Extrusion: Alkamax ML1810PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax ML1810PN have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight.&& |
| Product Description | |
|---|---|
| Supplier | Qenos |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Good flexibility,Food contact compliance,Broad Seal Range,Low density,Copolymer |
| Availabilitys | Asia Pacific |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 50 µ m | 183 | MPa | ASTM D882 |
| 2% secant, TD: 50 µ m | 190 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 50 µ m | 11.0 | MPa | ASTM D882 |
| TD, yield, 50 µ m | 11.0 | MPa | ASTM D882 |
| MD, fracture, 50 µ m | 50.0 | MPa | ASTM D882 |
| TD, fracture, 50 µ m | 46.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 50 µ m | 790 | % | ASTM D882 |
| TD, fracture, 50 µ m | 820 | % | ASTM D882 |
| Drop hammer impact | > 1500 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：50 µm | 580 | g | ASTM D1922 |
| TD：50 µm | 660 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 64 | ASTM D2457 | |
| Haze | |||
| 50 µm | 11 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.79 in/min |
| 3. 20 in/min |
| 4. F50 |
| 5. (10% LDPE blended) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |