| DAI-EL® G-551 DAI-EL G-551 is a cure incorporated terpolymer designed for transfer and compression molding applications molding. G-551 offers a good balance between methanol resistance and low temperature flexibility.&&DAI-EL® G-551 DAI-EL G-551 is a fluoroelastomer comprising terpolymer of vinylidenefluoride/tetrafluoroethylene/hexafluoropropylene, and contains a curing agent (bisphenol AF) and cure accelerator and demonstrates a good balance of solvent resistance and low temperature performance.&& |
| Product Description | |
|---|---|
| Supplier | Daikin Fluorochemicals |
| Generic | 氟橡胶 |
| Material Status | Commercial: Active |
| Features | Low temperature toughness,Terpolymer |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.84 to 1.89 | g/cm³ | |
| Mooney viscosity | |||
| ML 1+10，121℃ | 48 | MU | |
| Fluorine content | 69 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 74 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 25 ℃ | 15.9 | MPa | |
| 100% strain, 25 ℃ | 4.40 | MPa | |
| Tensile strain | |||
| Fracture, 25 ℃ | 210 | % | |
| tear strength | |||
| 25℃ | 20.6 | kN/m | |
| Compression deformation | |||
| 25℃，70 hr | 13 | % | |
| 100℃，70 hr | 9.0 | % | |
| 175℃，70 hr | 18 | % | |
| 200℃，70 hr | 25 | % |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 230℃，70 hr | 1.0 | % | |
| The rate of change in ultimate elongation in air | |||
| 230℃，70 hr | -1.0 | % | |
| The rate of change in hardness of a hardness tester in the air | |||
| Shore A, 230 ℃, 70 hr | 0.0 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -21.0 | ℃ |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| curing temperature | 170 | ℃ | |
| Curing time | |||
| Curelastmeter | 2.4 | min | |
| Gehman Torsion Test | |||
| T10 | -12 | ℃ | |
| T2 | -7 | ℃ | |
| TR Test | |||
| TR10 | -14 | ℃ | |
| TR70 | -8 | ℃ |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. 25% compression |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |