HOPELEX AG-3030

About
PC/ABS with balanced flowability, impact properties and hydrolytic stability Heat resistance&&

Product Description
SupplierLOTTE
GenericPC+ABS
Material StatusCommercial: Active
FeaturesHigh impact resistance,Hydrolysis stability,Good liquidity,High Heat Resistance,HB
AvailabilitysNorth America,Asia Pacific,Europe

Technical Data
PHYSICALNominal valueUnitTest method
Density1.10g/cm³ASTM D792
Shrinkage rate
MD0.50 to 0.70%ASTM D955

MECHANICALNominal valueUnitTest method
tensile strength
yield56.9MPaASTM D638
Tensile strain
fracture> 50%ASTM D638
Bending modulus2350MPaASTM D790
bending strength
yield86.3MPaASTM D790

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch ASTM D256
-30℃390J/mASTM D256
23℃,3.2mm590J/mASTM D256

THERMALNominal valueUnitTest method
Hot deformation temperature
1.8 MPa, unannealed105ASTM D648

FLAME CHARACTERISTICSNominal valueUnitTest method
Flame retardant level UL 94
1.20 mmHB UL 94
3.00 mmHB UL 94

Process Conditions
injectionNominal valueUnitTest method
Drying temperature80 to 90°C
Drying time4.0hr
Recommended maximum moisture content0.020%
Proposed maximum recycled material ratio20%
Hopper temperature60 to 80°C
Barrel rear temperature240 to 260°C
Barrel middle temperature240 to 260°C
Barrel front temperature230 to 250°C
Nozzle temperature240 to 260°C
Processing (melt) temperature240 to 260°C
Mold temperature60 to 80°C

Notes
1. Typical properties: these are not to be construed as specifications.
2. 2.0 in/min
3. 0.39 in/min
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.