| About |
|---|
| Carbon fiber-reinforced, graphite and PTFE-filled polyether ether ketone VESTAKEEP 2000 FC30 is a medium-viscosity, carbon fiber-reinforced, graphite and PTFEfilled polyether ether ketone for injection molding. Parts made of this resin can be used for bearing bushing or gearbox parts, due to the self-lubricating effect. The semi-crystalline polymer features superior mechanical, thermal, and chemical resistance. Parts made from VESTAKEEP 2000 FC30 are self-extinguishing. VESTAKEEP 2000 FC30 can be processed by common injection-molding machines for thermoplastics. We recommend a melt temperature between 370°C and 380°C during the injection molding process. If temperatures exceed 380°C, toxic gases can be released. Adequate ventilation and protective equipment must be provided. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C.&& |
| Product Description | |
|---|---|
| Supplier | Evonik |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | Self-lubricating,Self-extinguishing,Hypocrystalline,Solvent resistance,V-0 |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 380℃，5 kg | 15.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD：180℃，2.0 mm | 0.40 | % | ISO 294-4 |
| MD：180℃，2.0 mm | 0.10 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 11500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 145 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30 ℃, completely fractured | 5.0 | kJ/m² | ISO 179/1eA |
| 23 ℃, completely fractured | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30 ℃, completely fractured | 40 | kJ/m² | ISO 179/1eU |
| 23 ℃, completely fractured | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 320 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 337 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 340 | ℃ | ISO 306/A |
| — | 335 | ℃ | ISO 306/B |
| Melting temperature | 340 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 2.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+5 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+7 | ohms·cm | IEC 60093 |
| Relative permittivity | IEC 60250 | ||
| 50 Hz | 6.10 | IEC 60250 | |
| 1 MHz | 4.90 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | UL 94 | |
| Glowing wire flammability index | |||
| 2.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | |||
| 2 mm | 900 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 370 to 380 | °C | |
| Mold temperature | 160 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. determined on 2 mm sheets with film gate at rim mold temperature 180°C |
| 3. 2nd heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |