AMPLIFY™ EA 100

About
AMPLIFY™ EA 100 Functional Polymer is produced via a high-pressure reactor. This ethylene-ethyl acrylate (EEA) copolymer exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene. High performance packaging applications Polymer modification Tie layer to PVDC and Polyolefins Extrusion grade for profile and tubing Superior additive concentrate carrier Excellent thermal stability Complies with: U.S. FDA 21 CFR 175.105 U.S. FDA 21 CFR 177.1320 (with Restrictions) EU, No 10/2011 Consult the regulations for complete details.&&

About

AMPLIFY™ EA 100 Functional Polymer is produced via a high-pressure reactor. This ethylene-ethyl acrylate (EEA) copolymer exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene. High performance packaging applications Polymer modification Tie layer to PVDC and Polyolefins Extrusion grade for profile and tubing Superior additive concentrate carrier Excellent thermal stability Complies with: U.S. FDA 21 CFR 175.105 U.S. FDA 21 CFR 177.1320 (with Restrictions) EU, No 10/2011 Consult the regulations for complete details.&&

Product Description
Supplier	DOW
Generic	EEA
Material Status	Commercial: Active
Availabilitys	North America,Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.930	g/cm³	ASTM D792 , ISO 1183
Melt Flow Rate
190℃，2.16kg	1.3	g/10min	ASTM D1238，ISO 1133
Co monomer content	15.0	%	ASTM D3594

IMPACT	Nominal value	Unit	Test method
Tensile impact strength	无断裂		ASTM D1822

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	32.8	℃	ASTM D648
Embrittlement temperature	< -76.1	℃	ASTM D746
Vicat Softening Temp	67.2	℃	ASTM D1525 , ISO 306
Melting temperature
DSC	98.9	℃	Internal Method
Crystallization peak temperature
DSC	82.2	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness			ASTM D2240 , ISO 868
Shaw’s A	87		ASTM D2240 , ISO 868
Shaw’s D	37		ASTM D2240 , ISO 868
tensile strength			ASTM D638 , ISO 527-2
yield	3.79	MPa	ASTM D638 , ISO 527-2
fracture	17.9	MPa	ASTM D638 , ISO 527-2
Tensile strain			ASTM D638 , ISO 527-2
yield	8.0	%	ASTM D638 , ISO 527-2
fracture	750	%	ASTM D638 , ISO 527-2
Bending modulus
2% secant	66.9	MPa	ASTM D790B , ISO 178

Notes
1. Typical properties: these are not to be construed as specifications.
2. Calibration Range is 15 – 20% EA; Pathlength is normalized; Plaque/Film Thickness is 15 mil; Press Temperature is 160°C
3. Type S
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.