| Baydur 660 IBS is a black-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Compo- nent B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of contents of the drum to the day tank due to possible pigment settling. The Baydur 660 IBS system was designed for general-purpose applications and is used in industrial and recreational markets. The applications typically take advantage of the material’s strength, excellent surface finish, and large part capability. As with any product, use of the Baydur 660 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | PUR+MDI |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.399 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：6.35 mm | 0.30 to 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | Internal Method | ||
| — | 7.4 | kJ/m² | Internal Method |
| — | 8.0 | kJ/m² | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw D, 6.35 mm | 46 | ASTM D2240 | |
| Shore D, 12.70 mm | 49 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| Fracture, 6.35 mm | 8.27 | MPa | ASTM D638 |
| Fracture, 12.70 mm | 7.58 | MPa | ASTM D638 |
| Tensile strain | ASTM D638 | ||
| Fracture, 6.35 mm | 7.0 | % | ASTM D638 |
| Fracture, 12.70 mm | 9.0 | % | ASTM D638 |
| Bending modulus | ASTM D790 | ||
| 6.35 mm | 462 | MPa | ASTM D790 |
| 12.70 mm | 441 | MPa | ASTM D790 |
| bending strength | ASTM D790 | ||
| 6.35 mm | 13.8 | MPa | ASTM D790 |
| 12.70 mm | 16.5 | MPa | ASTM D790 |
| compressive strength | ASTM D695 | ||
| 6.35 mm | 7.93 | MPa | ASTM D695 |
| 12.7 mm | 7.58 | MPa | ASTM D695 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 12.7 mm | 104 | ℃ | ASTM D648 |
| Thermosetting components | |||
| Component A | 按重量计算的混合比: 120 | ||
| Component B | 按重量计算的混合比: 100 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |