RONFALIN® C C130

About
Perloy C130 is a high impact strength easy flow PC/ABS alloy with excellent sub-zero ductility. Having a vicat temp. of 130°C applications include electronic and automotive.&&

Product Description
Supplier	A. Schulman
Generic	PC+ABS
Material Status	Commercial: Active
Features	HB
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.15	g/cm³	ISO 1183
Melt Flow Rate
260℃，5.0kg	15	g/10min	ISO 1133
Shrinkage rate	0.50 to 0.70	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2400	MPa	ISO 527-2
tensile strength
yield	55.0	MPa	ISO 527-2
Tensile strain
fracture	> 50	%	ISO 527-2
Bending modulus	2300	MPa	ISO 178
bending strength	80.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃，Area	45.0	kJ/m²	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	108	℃	ISO 75-2/A
0.45 MPa, unannealed	125	℃	ISO 75-2/B
Vicat Softening Temp
B50	130	℃	ISO 306

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.