Plexar® PX3060

About
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).&&

About

Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).&&

Product Description
Supplier	LyondellBasell
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Availabilitys	North America,Latin America,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.924	g/cm³	ASTM D1505
Melt Flow Rate
190℃，2.16kg	2.2	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	51	µm
tensile strength			ASTM D882
MD, yield, 51 µ m, blow molded film	12.6	MPa	ASTM D882
TD, yield, 51 µ m, blow molded film	14.2	MPa	ASTM D882
MD, fracture, 51 µ m, blow molded film	30.1	MPa	ASTM D882
TD, fracture, 51 µ m, blow molded film	23.9	MPa	ASTM D882
Tensile strain			ASTM D882
MD, yield, 51 µ m, blow molded film	16	%	ASTM D882
TD, yield, 51 µ m, blow molded film	10	%	ASTM D882
MD, fracture, 51 µ m, blow molded film	760	%	ASTM D882
TD, fracture, 51 µ m, blow molded film	760	%	ASTM D882
Elmandorf tear strength			ASTM D1922
MD: 51 µ m, blow molded film	120	g	ASTM D1922
TD: 51 µ m, blow molded film	560	g	ASTM D1922
Water vapor transmittance
100% RH, 51 µ m, blow molded film	6.2	g/m²/24 hr	ASTM F372

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	100	℃	ASTM D1525

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	> 210	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.