| EVA resin ALCUDIA® PA-441 is recommended for hot melt adhesives and blends with waxes. It contains antioxidant and free flowing agent. TYPICAL APPLICATIONS Hot Melt Adhesives Packaging Bookbinding Carpet backing Blends with bitumen and asphalts Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Food contact compliance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 25 | g/10min | ISO 1133 |
| Vinyl acetate content | 28.0 | wt% | |
| viscosity | Internal Method | ||
| 150℃ | 2.90 | Pa·s | Internal Method |
| 175℃ | 1.60 | Pa·s | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shaw’s A | 78 | ISO 868 | |
| Shaw’s D | 26 | ISO 868 | |
| tensile strength | |||
| fracture | 12.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 790 | % | ISO 527-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 70.0 | ℃ | |
| Ring and Ball Softening Point | 120 | ℃ | ASTM E28 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blend 40:60 PA-441/wax |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |