| About |
|---|
| KEY FEATURES UmaPET HCM is high clear medium metallized film with excellent metal gloss. It exhibits good barrier properties along with good metal to film bond strength/adhesion. It has high gloss, excellent thermal stability, mechanical properties, flex crack resistance. APPLICATIONS UmaPET HCM is used as sandwich barrier layer in flexible packaging applications which provides high metal gloss & good barrier properties in laminates for confectionary, snacks, chips, extruded foods, tea etc.. Useful for high aesthetic appeal in decorative, holographic (temper evident & temper proof), textiles, glitters, label face stocks & surface printing applications.&& |
| Product Description | |
|---|---|
| Generic | PET |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good surface appearance,Good bond,Good tear strength,Electroplating,Block resin,Agglomerability |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | ASTM D1204 | ||
| MD：150℃，0.012 mm，30 min | 2.5 | % | |
| MD：150℃，0.015 mm，30 min | 2.5 | % | |
| MD：150℃，0.023 mm，30 min | 2.5 | % | |
| MD：150℃，0.036 mm，30 min | 2.5 | % | |
| MD：150℃，0.05 mm，30 min | 2.5 | % | |
| TD：150℃，0.012 mm，30 min | 0.40 | % | |
| TD：150℃，0.015 mm，30 min | 0.40 | % | |
| TD：150℃，0.023 mm，30 min | 0.40 | % | |
| TD：150℃，0.036 mm，30 min | 0.40 | % | |
| TD：150℃，0.05 mm，30 min | 0.40 | % | |
| surface tension | ASTM D2578 | ||
| 15.0 µm | 56 | mN/m | |
| 23.0 µm | 56 | mN/m | |
| 36.0 µm | 56 | mN/m | |
| 50.0 µm | 56 | mN/m | |
| Metallized side：12.0 µm | 56 | mN/m | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 12 15 23 36 | µm | |
| film thickness | 12, 15, 23, 36, 50 µm | ||
| tensile strength | ASTM D882 | ||
| MD, fracture, 12 µ m | 206 | MPa | |
| MD, fracture, 15 µ m | 186 | MPa | |
| MD, fracture, 23 µ m | 186 | MPa | |
| MD, fracture, 36 µ m | 177 | MPa | |
| MD, fracture, 50 µ m | 167 | MPa | |
| TD, fracture, 12 µ m | 216 | MPa | |
| TD, fracture, 15 µ m | 206 | MPa | |
| TD, fracture, 23 µ m | 206 | MPa | |
| TD, fracture, 36 µ m | 186 | MPa | |
| TD, fracture, 50 µ m | 186 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 100 | % | |
| MD, fracture, 15 µ m | 100 | % | |
| MD, fracture, 23 µ m | 100 | % | |
| MD, fracture, 36 µ m | 130 | % | |
| MD, fracture, 50 µ m | 130 | % | |
| TD, fracture, 12 µ m | 90 | % | |
| TD, fracture, 15 µ m | 90 | % | |
| TD, fracture, 23 µ m | 90 | % | |
| TD, fracture, 36 µ m | 120 | % | |
| TD, fracture, 50 µ m | 120 | % | |
| Oxygen permeability | ASTM D3985 | ||
| 23℃，12 µm | 0.900 | cm³/m²/24 hr | |
| 23℃，15 µm | 0.800 | cm³/m²/24 hr | |
| 23℃，23 µm | 0.800 | cm³/m²/24 hr | |
| 23℃，36 µm | 0.800 | cm³/m²/24 hr | |
| 23℃，50 µm | 0.800 | cm³/m²/24 hr | |
| Water vapor permeability | ASTM F1249 | ||
| — | 0.60 | g/m²/24 hr | |
| — | 0.60 | g/m²/24 hr | |
| — | 0.60 | g/m²/24 hr | |
| — | 0.60 | g/m²/24 hr | |
| — | 0.60 | g/m²/24 hr | |
| dosage | Internal Method | ||
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg | |
| 36.0 µm | 19.8 | m²/kg | |
| 50.0 µm | 14.3 | m²/kg |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Optical Density | Internal Method | ||
| 12.0 µm | -2.8 to 7.2 | % | |
| 15.0 µm | -2.8 to 7.2 | % | |
| 23.0 µm | -2.8 to 7.2 | % | |
| 36.0 µm | -2.8 to 7.2 | % | |
| 50.0 µm | -2.8 to 7.2 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |