| About |
|---|
| 30% Glass Reinforced, PA4T, Food Contact Quality, Drinking Water Grade |
| Product Description | |
|---|---|
| Supplier | DSM |
| Generic | PA 4T |
| Material Status | Commercial: Active |
| Features | Food contact compliance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Fracture stress | 210 | MPa | ISO 527-1/-2 |
| After adjustment | 190 | MPa | ISO 527-1/-2 |
| 80℃ | 180 | MPa | ISO 527-1/-2 |
| 120℃ | 150 | MPa | ISO 527-1/-2 |
| Fracture strain | 2.6 | MPa | ISO 527-1/-2 |
| After adjustment | 2.6 | MPa | ISO 527-1/-2 |
| 80℃ | 2.7 | MPa | ISO 527-1/-2 |
| 120℃ | 3 | MPa | ISO 527-1/-2 |
| Tensile modulus | 10500 | MPa | ISO 527-1/-2 |
| After adjustment | 10500 | MPa | ISO 527-1-2 |
| 80℃ | 10000 | MPa | ISO 527-1-2 |
| 120℃ | 9500 | MPa | ISO 527-1-2 |
| Bending modulus | 10000 | MPa | ISO 178 |
| bending strength | 290 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| 10℃ / min | 340 | ℃ | ISO 11357-1/-3 |
| Hot deformation temperature | |||
| 1.8 MPa | 320 | ℃ | ISO 75-1/2 |
| Flame retardant level | |||
| 0.80 mm | HB | Class | IEC 60695-11-10 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | >1E13 | ohm*m | IEC 60093 |
| After adjustment | >1E15 | ohms·cm | IEC 60093 |
| Dielectric strength | 45 | kv/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 600 | v | IEC 60112 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | ISO 179 / 1eU |
| -30℃ | 40 | kJ/m² | ISO 179 / 1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 9.9 | kJ/m² | ISO 179/1eA |
| -30℃ | 9 | kJ/m² | ISO 179/1eA |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.460 | g/cm³ | ISO 1183 |
| Water absorption rate | 2 | % | ISO 62 |
| Shrinkage rate | |||
| TD | 0.43 | % | ISO 527-1/-2 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 100 to 130 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Temperature at the rear of the barrel | 320 to 340 | °C | |
| Temperature in the middle of the barrel | 330 to 350 | °C | |
| Front temperature of material barrel | 330 to 350 | °C | |
| Nozzle temperature | 340 to 370 | °C | |
| Processing (melt) temperature | 340 to 370 | °C | |
| Mold temperature | 80 to 200 | °C | |
| Injection speed | 中等偏快 | ||
| Back pressure | 0.500 to 3.00 | MPa | |
| Screw compression ratio | 2.5:1.0 | ||
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |