| About |
|---|
| NatureFlex NM is available with the metallised surface wound facing either the inside or the outside of the reel.&& |
| Product Description | |
|---|---|
| Generic | 再生纤维 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Clarity,Good surface appearance,Good heat sealing,High elastic,Renewable resources,Retention of aroma ,Low odor,Biodegradable,Moisture resistance,Compostable,Grease resistance,Antistatic property,Low temperature heat sealing,Shading |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| Optical，23.3 µm | 2.50 | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 0.40 | ASTM D1894 | |
| With oneself – dynamic | 0.22 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 23 µ m | > 3000 | MPa | ASTM D882 |
| 1% secant, TD: 23 µ m | > 1500 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 23 µ m | 125 | MPa | ASTM D882 |
| TD, yield, 23 µ m | 70.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 23 µ m | 22 | % | ASTM D882 |
| TD, fracture, 23 µ m | 70 | % | ASTM D882 |
| Sealing emphasis | 2.7 | N/mm | Internal Method |
| Oxygen permeability (wet) (38 ℃, 23 µ m, 2.5% RH) | 3.00 | cm³/m²/24 hr | ASTM F1927 |
| Water vapor permeability | 10 | g/m²/24 hr | ASTM E96 |
| film thickness | 23.3 | µm | Internal Method |
| dosage | |||
| 23.3 µm | 29.9 | m²/kg | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Non-metallised surface, Thickness: 23.3 µ |
| 3. Metallised surface, Thickness: 23.3 µ |
| 4. Thickness: 23.3 µ |
| 5. 0 to 5% RH |
| 6. 38°C, 90%RH, thickness: 23.3 µ |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |