| SABIC® Vestolen A RELY 5922R 10000 is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its resistance against slow crack growth (SCG) the material SABIC® Vestolen A RELY 5922R 10000 is considered as PE100-RC and may be used for no dig applications. This material meets (inter)national standards for use in gas, drinking water and waste water piping. MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good tear strength,High density,Bimodal molecular weight distribution |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，2.16kg | < 0.10 | g/10min | ISO 1133 |
| 190℃，5.0kg | 0.20 | g/10min | ISO 1133 |
| Full incision creep test | |||
| ESCR(Environmental Stress Cracking Resistance), 80 ℃ | > 1 | yr | ISO 16770 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30 ℃, molded | 10 | kJ/m² | ISO 179/1eA |
| 23 ℃, molded | 26 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 72.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 45.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 72.0 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 124 to 128 | ℃ | DIN 53765 |
| Oxygen sensing time | |||
| Molded molding, 210 ℃ | > 20 | min | ISO 11357-6 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO 12162 |
| RAL Number | 9004 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 62 | ISO 868 | |
| Tensile modulus | |||
| 2 mm, molded into shape | 1100 | MPa | ISO 527-2/1BA/50 |
| tensile strength | |||
| Yield, 2 mm, molded | 24.0 | MPa | ISO 527-2/1BA/50 |
| Tensile strain | |||
| Yield, 2 mm, molded | 9.0 | % | ISO 527-2/1BA/50 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| Strain Hardening – Gp | > 50.0 | MPa | Internal Method |
| Notch Pipe Test | > 1 | yr | ISO 13479 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2% Arkopal N100, 4 MPa |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |