| Amodel® FC-1150 and FC-1150 L is an FDA compliant, 50% glass fiber reinforced resin designed for high strength and stiffness (and improved demolding properties for the L grades). This combines with its excellent thermal properties, low water absorption and good hydrolytic stability to make it particularly suited for components used in food service and consumer applications such coffee machines and ovens. Natural: FC-1150 (L) NT Black: FC-1150 (L) BK 946&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,Solvent resistance,Low moisture absorption,Chlorine-resistant |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ISO 1183/A |
| Shrinkage rate | ASTM D955 | ||
| MD：1.0 mm | 0.14 | % | ASTM D955 |
| MD：1.0 mm | 0.16 | % | ASTM D955 |
| MD：2.0 mm | 0.18 | % | ASTM D955 |
| MD：2.0 mm | 0.15 | % | ASTM D955 |
| Shrinkage rate | ASTM D955 | ||
| TD：1.00 mm | 0.42 | % | ASTM D955 |
| TD：1.00 mm | 0.46 | % | ASTM D955 |
| TD：2.0 mm | 0.43 | % | ASTM D955 |
| TD：2.0 mm | 0.42 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 19100 | MPa | ISO 527-2 |
| tensile strength | |||
| Fracture, 23 ℃ | 270 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 18400 | MPa | ISO 178 |
| bending strength | 400 | MPa | ISO 178 |
| Bending strain | |||
| 23℃ | 2.40 | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | 88 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 300 | ℃ | ISO 75-2/Af |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.030 to 0.060 | % | |
| Barrel rear temperature | 315 to 330 | °C | |
| Barrel middle temperature | 320 to 340 | °C | |
| Barrel front temperature | 325 to 345 | °C | |
| Processing (melt) temperature | 340 to 360 | °C | |
| Mold temperature | 160 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Pressure = 750 bar |
| 3. Pressure = 500 bar |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |