Vydyne® R633 - SOLIAO

About
Vydyne R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold release. Vydyne R633 has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass-reinforced PA66/6 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: Vydyne R633 has been used for many under-the-hood automotive applications, motor housings for power tools, and garden appliances. These resins have also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.&&

About

Vydyne R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold release. Vydyne R633 has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass-reinforced PA66/6 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: Vydyne R633 has been used for many under-the-hood automotive applications, motor housings for power tools, and garden appliances. These resins have also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.&&

Product Description
Supplier	Ascend
Generic	PA66/6
Material Status	Commercial: Active
Features	Good Rigidity,Good surface appearance,Good stripping performance,Lubricating,Good Tensile Strength,Copolymer
Availabilitys	North America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.39	g/cm³	ISO 1183
Shrinkage rate			ISO 294-4
TD：23℃，2.0 mm	0.90	%	ISO 294-4
MD：23℃，2.0 mm	0.40	%	ISO 294-4
Water absorption rate
Equilibrium, 23 ℃, 50% RH	2.3	%	ISO 62
23℃，24hr	1.3	%	ISO 62

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
23℃	10800	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	184	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	4.0	%	ISO 527-2
Bending modulus
23℃	8800	MPa	ISO 178
bending strength
23℃	255	MPa	ISO 178
Poisson’s ratio	0.40		ISO 527-2

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-30℃	11	kJ/m²	ISO 179
23℃	12	kJ/m²	ISO 179
Charpy Unnotch Impact strength			ISO 179
-30℃	44	kJ/m²	ISO 179
23℃	51	kJ/m²	ISO 179
Impact strength of cantilever beam notch			ISO 180
-30℃	12	kJ/m²	ISO 180
23℃	13	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	220	℃	ISO 75-2/A
0.45 MPa, unannealed	230	℃	ISO 75-2/B
Melting temperature	233	℃	ISO 11357-3
Linear coefficient of thermal expansion
TD：23~55℃，2 mm	1.0E-4	1/℃	ISO 11359-2
MD：23~55℃，2 mm	1.5E-5	1/℃	ISO 11359-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Proposed maximum recycled material ratio	25	%
Barrel rear temperature	280 to 310	°C
Barrel middle temperature	280 to 310	°C
Barrel front temperature	280 to 310	°C
Nozzle temperature	280 to 310	°C
Processing (melt) temperature	285 to 305	°C
Mold temperature	65 to 95	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.