ARLEN™ AE4200 (Dry) ARLEN™ AE4200 is a Polyamide 6T (Nylon 6T) material. It is available in North America. Primary attribute of ARLEN™ AE4200: Flame Rated.&&ARLEN™ AE4200 ARLEN™ AE4200 by Mitsui Chemicals is a modified polyamide 6T grade. Possesses high dimensional stability, high melting point, minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity even in a high-temperature atmosphere such as the inside of an engine room. Is suitable for processing by injection molding. ARLEN™ AE4200 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment. Complies with UL 94 HB flame rating. Features: Possesses high dimensional stability, high melting point, minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance with high rigidity. Applications: ARLEN™ AE4200 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment.&&

About

ARLEN™ AE4200 (Dry) ARLEN™ AE4200 is a Polyamide 6T (Nylon 6T) material. It is available in North America. Primary attribute of ARLEN™ AE4200: Flame Rated.&&ARLEN™ AE4200 ARLEN™ AE4200 by Mitsui Chemicals is a modified polyamide 6T grade. Possesses high dimensional stability, high melting point, minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity even in a high-temperature atmosphere such as the inside of an engine room. Is suitable for processing by injection molding. ARLEN™ AE4200 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment. Complies with UL 94 HB flame rating. Features: Possesses high dimensional stability, high melting point, minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance with high rigidity. Applications: ARLEN™ AE4200 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment.&&

Product Description
Supplier	Mitsui
Generic	PA 6T
Material Status	Commercial: Active
Features	HB
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ASTM D792
Shrinkage rate
TD：2.0 mm	0.90	%	ASTM D955
MD：2.0 mm	0.90	%	ASTM D955
Water absorption rate			ASTM D570
23℃，24hr	0.40	%	ASTM D570
100℃，24hr	2.6	%	ASTM D570

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	200	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	135	℃	ASTM D648
Glass transition temperature	125	℃	DSC
Melting temperature	320	℃
Linear coefficient of thermal expansion
TD	8.2E-5	1/℃	ASTM D696
MD	8.0E-5	1/℃	ASTM D696

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	1.0E+16	ohms·cm	ASTM D257
Dielectric strength	23	kV/mm	ASTM D149
Dielectric constant
1 MHz	3.30		ASTM D150
Dissipation factor
1 MHz	0.018		ASTM D150

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB		UL 94

MECHANICAL	Nominal value	Unit	Test method
tensile strength
2 mm	80.0	MPa	ASTM D638
Tensile strain
Fracture, 2 mm	50	%	ASTM D638
Bending modulus	2400	MPa	ASTM D790
bending strength	110	MPa	ASTM D790
Rockwell hardness			ASTM D785
M-level	65		ASTM D785
R-level	—		ASTM D785

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	110	°C
Drying time	2.0 to 6.0	hr
Hopper temperature	50 to 90	°C
Barrel rear temperature	315 to 330	°C
Barrel middle temperature	320 to 335	°C
Barrel front temperature	325 to 340	°C
Nozzle temperature	325 to 340	°C
Mold temperature	50 to 90	°C
Injection speed	Moderate
Screw speed	150	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.