| Braskem PE SGF4960 SGF4960 is a homopolymer high-density polyethylene, developed for the blow-molding segment with high density and stiffness combined with high impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bottles for food applications such as dairy products and beverages; Rigid containers for non-food applications such as cosmetics and lubricant oils; Caps & closures molded by compression; Rigid containers for pharmaceutical applications (complies with USP 33). Process: Blow Molding.&&Braskem PE SGF4960 SGF4960 is a homopolymer high-density polyethylene, developed for the blow-molding segment with high density and stiffness combined with high impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bottles for food applications such as dairy products and beverages; Rigid containers for non-food applications such as cosmetics and lubricant oils; Caps & closures molded by compression; Rigid containers for pharmaceutical applications (complies with USP 33). Process: Blow Molding.&&Braskem PE SGF4960 SGF4960 is a homopolymer high-density polyethylene, developed for the blow-molding segment with high density and stiffness combined with high impact resistance. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bottles for food applications such as dairy products and beverages; Rigid containers for non-food applications such as cosmetics and lubricant oils; Caps & closures molded by compression; Rigid containers for pharmaceutical applications (complies with USP 33). Process: Blow Molding.&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Renewable resources,Food contact compliance,No BPA,High density,Homopolymer |
| Availabilitys | North America,Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.962 | g/cm³ | ASTM D792 |
| Melt Flow Rate | ASTM D1238 | ||
| 190℃，2.16kg | 0.34 | g/10min | ASTM D1238 |
| 190℃，21.6kg | 28 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 | 25.0 | hr | ASTM D1693 |
| Biobased Content | 96 | % | ASTM D6866 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 64 | ASTM D2240 | |
| tensile strength | |||
| Fracture, molded | 35.0 | MPa | ASTM D638 |
| Yield, molding | 30.0 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% cut, molded | 1400 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | |||
| Compression Molding | 230 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, molded | 79.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 129 | ℃ | ASTM D1525 2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |