| Product Description | |
|---|---|
| Generic | PP+EPDM |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 15.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 45 | kJ/m² | ISO 179/1eU |
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 108 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 62.0 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 39.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1700 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 22.0 | MPa | ISO 527-2/50 |
| fracture | 20.3 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 4.0 | % | ISO 527-2/50 |
| fracture | 54 | % | ISO 527-2/5 |
| Bending modulus | 2050 | MPa | ISO 178 |
| bending strength | 30.0 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |