Amodel® DW-1150

About
Amodel® DW-1150 is a 50% glass-fiber-reinforced resin designed for high strength and stiffness and improved hydrolytic stability. This material has low moisture absorption and a low coefficient of thermal expansion, which means excellent dimensional stability. Creep resistance is also exceptional. This grade has been approved for use with potable water in the United States, France, Germany, and the United Kingdom. Black: DW-1150 BK938&&

About

Amodel® DW-1150 is a 50% glass-fiber-reinforced resin designed for high strength and stiffness and improved hydrolytic stability. This material has low moisture absorption and a low coefficient of thermal expansion, which means excellent dimensional stability. Creep resistance is also exceptional. This grade has been approved for use with potable water in the United States, France, Germany, and the United Kingdom. Black: DW-1150 BK938&&

Product Description
Supplier	Solvay
Generic	PPA
Material Status	Commercial: Active
Features	Good Rigidity,Good flexibility,Good Dimensional Stability,Solvent resistance,Low moisture absorption,Chlorine-resistant
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.68	g/cm³	ISO 1183/A

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	18000	MPa	ISO 527-2
tensile strength
Fracture, 23 ℃	260	MPa	ISO 527-2
Tensile strain
Fracture, 23 ℃	1.9	%	ISO 527-2
Bending modulus
23℃	18500	MPa	ISO 178
bending strength
Fracture, 23 ℃	400	MPa	ISO 178
Fracture bending strain
23℃	2.3	%	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	12	kJ/m²	ISO 179
Charpy Unnotch Impact strength	80	kJ/m²	ISO 179
Impact strength of cantilever beam notch	12	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	300	℃	ISO 75-2/Af

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0	hr
Recommended maximum moisture content	0.030 to 0.060	%
Barrel rear temperature	315 to 330	°C
Barrel middle temperature	320 to 340	°C
Barrel front temperature	325 to 345	°C
Processing (melt) temperature	340 to 360	°C
Mold temperature	160	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.