| Product Description | |
|---|---|
| Supplier | SUQING |
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Hardness |
| Availabilitys | China |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Modulus | 2800 | MPa | ISO 527 |
| Tensile Strength | |||
| Yield yld | 80 | MPa | ISO 527 |
| Tensile Strain | |||
| Yield yld | 20 | % | ISO 527 |
| Pencil hardness | 1H | ASTM D3363 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 18 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| B50 | 110 | ℃ | ISO 306 |
| Heat Deformation Temperature | |||
| 1.8 MPa | 105 | ℃ | ISO 75 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 2mm | V-2 | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shrinkage rate | 0.4-0.7 | % | ISO 294 |
| Melt Volume Rate | |||
| 230℃，3.8kg | 15 | cm³/10min | ISO 1133 |
| 1.20 | g/cm³ | ISO 1183 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Light Transmission | |||
| 1mm，D65 | 92 | % | ISO 13468 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Drying Temperature | 100 | ℃ | |
| Drying Time | 4-6 | h | |
| Melt Temperature | 220-260 | ℃ | |
| Mold Temperature | 60-100 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |