| A High Performance Sponge Polymer Unique Features Very high Molecular weight Ultra fast curing Improved abrasion resistance High tensile strength and high tear resistance High wrinkle resistance while maintaining soft compression deflection Excellent green strength for extruded profile shape stability Rapid Banbury mixing and excellent dispersion properties Extended with a white, hydrotreated paraffinic oil Applications TPO and TPV Automotive closed cell sponge extrusions and molded sponge corners Closed cell sheet sponge Dynamic applications&& |
| Product Description | |
|---|---|
| Generic | EPDM+SEBS |
| Material Status | Commercial: Active |
| Features | Good Green Strength,Ultra high molecular weight,Good Tensile Strength,Oil charge,Good tear strength,Good wear resistance,Fast Cure |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.880 | g/cm³ | ASTM D792 |
| Mooney viscosity | |||
| ML 1+4，125℃ | 48 | MU | Internal Method |
| Ethylidene norbornene content | 8.5 | wt% | Internal Method |
| oils | |||
| Paraffin oil | 75.0 | phr | Internal Method |
| Stabilizer | Non-staining | ||
| molecular weight distribution | Medium | Internal Method | |
| Volatiles | < 0.70 | wt% | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Unmilled |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |