Polifil® TPO 60D12UV

About
Polifil ® TPO-60D12UV is a UV stabilized injection molding grade of compounded TPO utilizing metallocine catalyst technology. This product is intended for applications requiring outstanding impact properties at both ambient and low temperatures needing UV stabilization. Typical applications include automotive bumper and fascia components, recreational vehicle cowls, and lawn and garden machinery guards. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations to meet your application requirements.&&

About

Polifil ® TPO-60D12UV is a UV stabilized injection molding grade of compounded TPO utilizing metallocine catalyst technology. This product is intended for applications requiring outstanding impact properties at both ambient and low temperatures needing UV stabilization. Typical applications include automotive bumper and fascia components, recreational vehicle cowls, and lawn and garden machinery guards. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations to meet your application requirements.&&

Product Description
Generic	PO增强
Material Status	Commercial: Active
Features	Weather resistance is good,Low warping,High impact resistance,Low contractility,low-temperature impact resistance
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	12	g/10min	ASTM D1238
Shrinkage rate
MD	1.8	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-18℃	20.0	kJ/m²
23℃	> 54.0	kJ/m²
Drop hammer impact
23℃，12.7 mm	40.0	J	ASTM D5420

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	74.0	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	60		ASTM D955
tensile strength
Yield, 23 ℃	19.1	MPa	ASTM D638
Tensile strain
Fracture, 23 ℃	> 500	%	ASTM D638
Bending modulus
1% secant, 23 ℃	790	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	82 to 99	°C
Drying time	1.0 to 2.0	hr
Barrel rear temperature	199 to 210	°C
Barrel middle temperature	210 to 216	°C
Barrel front temperature	216 to 221	°C
Nozzle temperature	221 to 227	°C
Processing (melt) temperature	204 to 232	°C
Mold temperature	10 to 60	°C
Injection speed	快速
Back pressure	0.345 to 0.689	MPa
Screw speed	50 to 100	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.