| About |
|---|
| Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PET |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Sprayable,Low contractility |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 265℃，5 kg | 15.0 | cm³/10min | ISO 1133 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.42 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.14 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4150 | MPa | ISO 527-1-2 |
| Tensile stress | |||
| yield | 56.0 | MPa | |
| fracture | 50.0 | MPa | |
| Tensile strain | |||
| yield | 3.2 | % | |
| fracture | 8.0 | % | |
| Bending modulus | 4050 | MPa | ISO 178 |
| Bending stress | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.0 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 8.0 | kJ/m² | |
| Notched impact strength of cantilever beam | |||
| -30℃ | 80 | kJ/m² | |
| 23℃ | 100 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 4.0 mm, 64 mm span | 110 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 137 | ℃ | ISO 306 |
| — | 140 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：-30~80℃ | 5.2E-5 | 1/℃ | |
| TD：-30~80℃ | 7.2E-5 | 1/℃ |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 110 to 120 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Temperature at the rear of the barrel | 240 to 270 | °C | |
| Temperature in the middle of the barrel | 250 to 275 | °C | |
| Front temperature of material barrel | 260 to 280 | °C | |
| Nozzle temperature | 260 to 275 | °C | |
| Processing (melt) temperature | 265 to 275 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |