| About |
|---|
| Impact modified PBT+PC resin. Outdoor enclosure. Not available in all colors.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC+PBT |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 266℃，5.0kg | 19 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 265℃，5 kg | 17.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.2 to 1.4 | % | |
| TD：3.2 mm | 1.2 to 1.4 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1960 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 48.0 | MPa | |
| fracture | 39.0 | MPa | |
| Tensile strain | |||
| yield | 6.0 | % | |
| fracture | 50 | % | |
| Bending modulus | |||
| 50 mm span | 1990 | MPa | ASTM D790 |
| bending strength | |||
| Yield, 50 mm span | 78.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 670 | J/m | ASTM D256 |
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 49.0 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 126 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 85.0 | ℃ | |
| Vicat Softening Temp | 135 | ℃ | ASTM D1525 6 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 7.9E-5 | 1/℃ | |
| TD：-40~40℃ | 8.6E-5 | 1/℃ | |
| Relative temperature index | 100 | ℃ | UL 746 |
| Electrical performance | 100 | ℃ | UL 746 |
| Impact mechanical performance | 85.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Arc resistance | PLC 6 | ASTM D495 | |
| Compared to the leakage tracing index | PLC 2 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 4 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 120 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Recommended injection volume | 40 to 80 | % | |
| Barrel rear temperature | 240 to 255 | °C | |
| Barrel middle temperature | 245 to 260 | °C | |
| Barrel front temperature | 250 to 265 | °C | |
| Nozzle temperature | 245 to 260 | °C | |
| Processing (melt) temperature | 250 to 265 | °C | |
| Mold temperature | 65 to 90 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 50 to 80 | rpm | |
| Vent depth | 0.025 to 0.038 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. Type I, 2.0 in/min |
| 4. 0.051 in/min |
| 5. Rate A (50°C/h), Loading 2 (50 N) |
| 6. Tungsten Electrode |
| 7. Surface |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |