| LNP* THERMOCOMP* YX12401 is a compound based on Polyester Elastomer containing proprietary fillers. Also known as: LNP* THERMOCOMP* Compound YX12401 Product reorder name: YX12401&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | TPEE |
| Material Status | Commercial: Negative |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| Shrinkage rate | ASTM D955 | ||
| MD：24 hrs | 2.2 | % | ASTM D955 |
| TD：24 hrs | 2.2 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr，50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.32 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 382 | MPa | ASTM D638 |
| — | 412 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 22.0 | MPa | ASTM D638 |
| yield | 22.0 | MPa | ISO 527-2/5 |
| fracture | 33.0 | MPa | ASTM D638 |
| fracture | 31.0 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| yield | 28 | % | ASTM D638 |
| yield | 28 | % | ISO 527-2/5 |
| Bending modulus | |||
| 50 mm span | 321 | MPa | ASTM D790 |
| — | 318 | MPa | ISO 178 |
| bending strength | 14.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | |||
| 23℃，Total Energy | 33.0 | J | ASTM D3763 |
| — | 41.8 | J | ISO 6603-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 112 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed, 64 mm span | 87.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.2 mm | 47.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 64 mm span | 49.0 | ℃ | ISO 75-2/Af |
| Linear coefficient of thermal expansion | ASTM D696 | ||
| MD：-30~30℃ | 2.0E-4 | 1/℃ | ASTM D696 |
| TD：-30~30℃ | 1.7E-4 | 1/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 182 to 193 | °C | |
| Barrel middle temperature | 204 to 216 | °C | |
| Barrel front temperature | 227 to 238 | °C | |
| Processing (melt) temperature | 216 to 238 | °C | |
| Mold temperature | 27 to 54 | °C | |
| Back pressure | 0.172 to 0.344 | MPa | |
| Screw speed | 30 to 60 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |