| Baytec GS-V85A is a two-component, one-shot system that yields a solid polyurethane elastomer. The isocyanate component is an isocyanate-terminated (MDI) polyester prepolymer, and the polyol component is a polyethylene/polybutylene adipate diol. The Baytec GS-V85A system is used in the production of cast polyurethane elastomers. As with any product, use of the Baytec GS-V85A system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.&& |
| Product Description | |
|---|---|
| Supplier | Covestro |
| Generic | TSU |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shaw’s A | 93 | ASTM D2240 | |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 47.5 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 480 | % | ASTM D412 |
| tear strength | |||
| — | 96.3 | kN/m | ASTM D624 |
| cracking | 49 | kN/m | ASTM D1938 |
| Compression deformation | |||
| 70℃，22 hr | 19 | % | ASTM D395B |
| Basho’s elasticity | 41 | % | ASTM D2632 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermosetting components | |||
| Part C | 按重量计算的混合比: 15 | ||
| Component A | 按重量计算的混合比: 97 | ||
| Component B | 按重量计算的混合比: 85 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |