Braskem PE LL6800N

About
LL6800N resin is a Linear Low Density Polyethylene for blown film extrusion with excellent mechanical properties. Applications: Heavy-duty bags; liners; LDPE and HDPE blends; packages for general use. Additive: Antiblocking Processing Aid Process: LL6800N resin should be processed on specific extruders for LLDPE. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 200 to 220° and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1.&&

About

LL6800N resin is a Linear Low Density Polyethylene for blown film extrusion with excellent mechanical properties. Applications: Heavy-duty bags; liners; LDPE and HDPE blends; packages for general use. Additive: Antiblocking Processing Aid Process: LL6800N resin should be processed on specific extruders for LLDPE. The optimum processing conditions will vary according to the type of equipment used, but the best results are obtained at a melt temperature within the range of 200 to 220° and blends with LDPE with a maximum ratio of 30%. Recommended blow up ratio: 1.8 to 3:1.&&

Product Description
Supplier	Braskem
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Features	High anti-blocking,Inoxidizability,Octene copolymer
Availabilitys	Latin America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.921	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.75	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
tensile strength
TD, fracture, 100 µ m, blow molded film	40.0	MPa	ASTM D882
MD, fracture, 100 µ m, blow molded film	40.0	MPa	ASTM D882
Tensile strain
TD, fracture, 100 µ m, blow molded film	1300	%	ASTM D882
MD, fracture, 100 µ m, blow molded film	1200	%	ASTM D882
Bending modulus
1% secant, TD, 100 µ m, blow molded film	240	MPa	ASTM D790
1% secant, MD, 100 µ m, blow molded film	200	MPa	ASTM D790
Drop hammer impact
100 µ m, blow molded film	490	g	ASTM D1709
tear strength
TD, 100 µ m, blow molded film	2100	g	ASTM D1922
MD, 100 µ m, blow molded film	870	g	ASTM D1922

optical performance	Nominal value	Unit	Test method
gloss
60 °, 100 µ m, blow molded film	100		ASTM D2457
Haze
100 µ m, blow molded film	19	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.