This product is classified as an amorphous thermoplastic blend of ABS and Polycarbonate. This product is known for high impact and notched impact strength, stiffness, heat resistance, dimensional accuracy, low shrinkage, low warp, and light stability. This product is available in: Non-reinforced general purpose Non-reinforced flame retardant Glass fiber reinforced Acrylic co-extruded cap Applications: Some ideal application for Prime PC/ABS include the following: Engine covers Fan shrouds Structural parts Motorcycle fairings Processing: Forming temp. is 400°F, tool temperature is 150-200°F. The part can be de-molded at 200°F. Sheet should be dried before forming @ 180°F for 2-4 hrs. Finishing: Cutting or machining of this product may be done by sawing, drilling, grinding, sanding, punching and die cutting. High pressure and laser cutting will also work for this product. Prime PC/ABS may be bonded with chemical, mechanical screws and other type of fasteners as well as sonic welding. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: PC/ABS can be color matched to suit your needs. Several textures are available including, H/C, FL/HC, Calf Grain and more. Sheet thickness can range from .090-.400 and in widths of up to 120″.&&

About

This product is classified as an amorphous thermoplastic blend of ABS and Polycarbonate. This product is known for high impact and notched impact strength, stiffness, heat resistance, dimensional accuracy, low shrinkage, low warp, and light stability. This product is available in: Non-reinforced general purpose Non-reinforced flame retardant Glass fiber reinforced Acrylic co-extruded cap Applications: Some ideal application for Prime PC/ABS include the following: Engine covers Fan shrouds Structural parts Motorcycle fairings Processing: Forming temp. is 400°F, tool temperature is 150-200°F. The part can be de-molded at 200°F. Sheet should be dried before forming @ 180°F for 2-4 hrs. Finishing: Cutting or machining of this product may be done by sawing, drilling, grinding, sanding, punching and die cutting. High pressure and laser cutting will also work for this product. Prime PC/ABS may be bonded with chemical, mechanical screws and other type of fasteners as well as sonic welding. Please contact your Primex Plastics representative for more information on finishing, fabricating, or the thermoforming process. Colors, Textures and Capabilities: PC/ABS can be color matched to suit your needs. Several textures are available including, H/C, FL/HC, Calf Grain and more. Sheet thickness can range from .090-.400 and in widths of up to 120″.&&

Product Description
Generic	PC+ABS
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Low warping,High impact resistance,Good Dimensional Stability,Low contractility,Machinable,High Heat Resistance,Ultrasonic soldering,Agglomerability,Amorphous
Availabilitys	North America,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.22	g/cm³	ASTM D792
Water absorption rate
23℃，24hr	0.10	%	ASTM D570

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	3300	MPa	ASTM D638
tensile strength			ASTM D638
yield	55.8	MPa	ASTM D638
fracture	60.0	MPa	ASTM D638
Bending modulus	2990	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	430	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature			ASTM D648
0.45 MPa, unannealed	138	℃	ASTM D648
1.8 MPa, unannealed	126	℃	ASTM D648
Vicat Softening Temp	118	℃	ASTM D1525
Linear coefficient of thermal expansion
MD	6.6E-5	1/℃	ASTM E831

Supplementary information	Nominal value	Unit
De（mold Temperature）	93	℃
Tool Temperature	66 to 93	℃
Forming temperature	204	℃
drying temperature	82	℃

Notes
1. Typical properties: these are not to be construed as specifications.
2. 2 to 4 hrs
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.