| About |
|---|
| HB600TF is a low melt flow rate polypropylene homopolymer intended for extrusion and thermoforming . Its very good organoleptic properties allows this grade to be used with any masterbatch without discoloring problems. CAS-No.: 9003-07-0 Applications HB600TF is recommended for: In line and off line thermoforming Mixing with copolymer House ware and thin wall packaging Textile film yarns Margarine tubs Woven fabrics, ropes and twines Special Features HB600TF is optimised to deliver: Very good processability Good contact clarity Very good melt stability stiffness and impact balance&& |
| Product Description | |
|---|---|
| Supplier | Borealis AG |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good Clarity,Low liquidity,High impact resistance,Renewable resources,Good sensory characteristics.,Homopolymer,Higher melt stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1400 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 33.5 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| yield | 10 | % | ISO 527-2/50 |
| Bending modulus | 1300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 86.0 | ℃ | ISO 75-2/B |
| Melting temperature | |||
| DSC | 162 to 166 | ℃ | ISO 3146 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Disk |
| 3. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |