| Daelim Po1y® VL0001 is an Ethylene-based Plastomer product. It is available in Asia Pacific or Europe. Applications of Daelim Po1y® VL0001 include additive/masterbatch, film and food contact applications. Characteristics include: Good Sealability Antiblock Antioxidant Clarity Good Toughness&& |
| Product Description | |
|---|---|
| Generic | 乙烯基辛烯塑料 |
| Material Status | Commercial: Active |
| Features | Good Clarity,Good flexibility,Good heat sealing,Smoothness,High anti-blocking,Inoxidizability,Low temperature heat sealing |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 50 µ m, blow molded film | 44.1 | MPa | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 45.1 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 50 µ m, blow molded film | 640 | % | ASTM D882 |
| MD, fracture, 50 µ m, blow molded film | 590 | % | ASTM D882 |
| Drop hammer impact | |||
| 50 µ m, blow molded film | > 930 | g | ASTM D1709-B |
| Initial sealing temperature | |||
| 50 µ m, blow molded film | 92.0 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 86.0 | ℃ | ASTM D1525 |
| Melting peak temperature | 95.0 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20 °, 50 µ m, blow molded film | 112 | ASTM D2457 | |
| Haze | |||
| 50 µ m, blow molded film | 3.2 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HGT, 2.8 kg, 0.5 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |